UNS N02201 (Nickel 201) Werkstoff 2.4068
UNS N02201, Nickel 201, wrought commercially pure nickel, is a reduced carbon version of N02200. exhibiting improved corrosion resistance at temperatures above 300°C avoiding graphite precipitation.
Data Sheet
UNS N02201, Nickel 201, wrought commercially pure nickel, is a reduced carbon version of N02200. exhibiting improved corrosion resistance at temperatures above 300°C avoiding graphite precipitation.
ASTM Specifications:- Sheet and plate ASTM B162, Bar and rod ASTM B160, Seamless pipe ASTM B161, Pipefittings ASTM B366, Forgings ASTM B564
CLICK HERE TO FIND A SUPPLIER OR STOCKIST
Applications
- Chemical Processing
- Aerospace
- Food processing Industry
Chemical Composition
| C |
(Carbon) |
0.02% Max |
| Fe |
(Iron) |
0.40% Max |
| Mn |
(Manganese) |
0.35% Max |
| Si |
(Silicon) |
0.35% Max |
| S |
(Sulphur) |
0.01% Max |
| Cu |
(Copper) |
0.25% Max |
| Ni |
(Nickel) |
99.0% Min |
Physical
| Density |
8900kg/m3 |
| Melting range |
1435-1446ºC |
Mechanical
| Hardness Rockwell B |
45-80 |
| Tensile Strength @ Break |
403 Mpa / 58500psi |
| Tensile Strength @ Yield |
103Mpa / 14900 psi 0.2% offset |
| Elongation in 2" |
50% |
| Modulus of Elasticity in tension |
207Gpa 30000 ksi |
* Above properties typical values of annealed material at room temp
Thermal
| CTELinear |
13.3 μm/m-ºC (@temp 27-93ºC) |
| |
14.4 μm/m-ºC (@temp 27-316ºC) |
| Specific Heat Capacity |
0.456J/g-ºC @ 0-100ºC |
Current rating is 0.00. Total votes 0.
Although Engineering Alloys endevours to ensure the accuracy of the information provided, we accept no liability in
connection with information provided in this data sheet. This data should not be acted upon without further research,
consultation and testing. Material properties can vary from one manufacturer to another. See out terms and conditions of use.